| 1 | Erratum to: Sn^(4+) precursor enables 12.4% efficient kesterite solar cell from DMSO solution with open circuit voltage deficit below 0.30 V (vol 64, issue 1, page 52, 2021)显示文摘In the version of the article originally published in volume 64,issue 1,2021 of Sci China Mater(2021,64(1):52–60,http://gffzzd3cc09b8251d45dfsw5qnkoq9qpn660co.ffgz.tsg.suse.edu.cn/10.1007/s40843-020-1408-x),the chemical formula of Sn(DMSO)_(4)Cl_(4)(page 54,8^(th) line in the left column;page 56,4^(th) and 6^(th) lines from the bottom of left column and in Equations(6 and 7)in the right column)was miswritten.The correct formula should be as below:SN(DMSO)_(2)CL_(4). | Yuancai Gong Yifan Zhang Erin Jedlicka Rajiv Giridharagopal James A.Clark Weibo Yan Chuanyou Niu Ruichan Qiu Jingjing Jiang Shaotang Yu Sanping Wu Hugh W.Hillhouse David S.Ginger Wei Huang Hao Xin | 2021 | Science China Materials2021，64，5： | 7 |
| 2 | 全面积效率12.4%、开路电压损失低于0.30 V的CZTSSe太阳能电池:Sn^4+前驱体在DMSO溶液中的使用显示文摘开路电压损失(Voc,def)大是制约锌黄锡矿结构CZTSSe太阳能电池效率的关键因素,目前世界纪录效率(12.6%)CZTSSe电池的Voc,def为0.345 V.本文分别以SnCl4和SnCl2·2H2O为锡前驱体研究二甲基亚砜(DMSO)溶液法制备的CZTSSe太阳能电池的开路电压损失问题.研究发现不同价态的锡前驱体化合物与有机配体硫脲(Tu)和溶剂DMSO发生不同的配位反应,使得从溶液到CZTSSe吸光层薄膜的反应路径截然不同.Sn^2+与Tu配位导致前驱体薄膜中SnS、ZnS和Cu2S的生成,这些硫化物在硒化过程中首先转化成硒化物而后逐步熔合生成CZTSSe,其反应路径中多物相的转化和熔合导致薄膜光电性能差,由该薄膜获得的最优器件有效面积效率仅为8.84%,Voc,def为0.391 V.而Sn^4+与DMSO配位,该前驱体溶液经退火直接得到组成均匀的CZTS前驱体薄膜,在硒化过程中CZTS直接发生取代反应生成CZTSSe,得到的CZTSSe薄膜组成均匀,光电性能优异,由该薄膜制备的器件有效面积效率达到12.2%,Voc,def降低至0.344 V.此外,CZTSSe薄膜性质的不同导致CZTSSe/CdS异质结热处理(JHT)结果的不同.JHT显著提高了Sn4+器件的性能,却略微降低了Sn^2+器件的性能.最终,由Sn4+溶液获得了全面积效率为12.4%,有效面积效率高达13.6%,Voc,def低至0.297 V的CZTSSe太阳能电池器件.研究结果表明通过控制溶液中化学组成获得组成均匀的CZTS预制膜是获得高效CZTSSe电池薄膜材料和降低器件Voc,def的关键.本报道不仅为进一步提高CZTSSe电池效率提供了新的思路,而且实现了Voc,def首次低于0.30 V,预示了CZTSSe未来的应用前景. | 龚元才 张一凡 Erin Jedlicka Rajiv Giridharagopal James A.Clark 闫伟博 牛传友 邱瑞婵 江晶晶 余绍棠 吴三平 Hugh W.Hillhouse David S.Ginger 黄维 辛颢 | 2021 | Science China Materials2021，64，1： | 4 |
您所在的机构暂未开通此部分的功能，请联系管理员