题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Transformation of Laves phases and its effect on the mechanical properties of TIG welded Mg-Al-Ca-Mn alloys显示文摘The effects of Al content and Ca/Al mass ratio on the microstructure and mechanical properties of tungsten inert gas(TIG)welded Mg-2Ca-x Al-0.5Mn(x=0,1,5)alloy joints were studied in present work.Results showed that increasing Al content was effective in reducing the dendrite spacing at the fusion zone(FZ)edge.The Laves phases in the FZ and the heat-affected zone(HAZ)can be changed from Mg_(2)Ca to(Mg,Al)_(2)Ca with the decrease of Ca/Al ratio,and the(Mg,Al)_(2)Ca could be further transformed to Al_(2)Ca under welding thermal cycle.Furthermore,dynamic dissolution and precipitation of Laves phases and Al_(8)Mn_(5)phases occurred in the HAZ,resulting in a gradient microstructure and hardness peak in this area.The tensile properties of the joints were significantly improved with the increase of Al content,which was mainly due to the modification of Laves phases. | Sensen Chai Shiyu Zhong Qingshan Yang Daliang Yu Qingwei Dai Hehe Zhang Limeng Yin Gang Wang Zongxiang Yao | 2022 | Journal of Materials Science & Technology2022，，25： | 2 |
| 2 | Influence of rolling speed on microstructure and mechanical properties of AZ31 Mg alloy rolled by large strain hot rolling显示文摘 | Fei Guo Dingfei Zhang Xusheng Yang Luyao Jiang Sensen Chai Fusheng Pan | 2014 | Materials Science & Engineering A2014，，： | 1 |
| 3 | Solid-state bonding process induced highly synergistic mechanical properties of 6061 Al alloy joint by shear deformation显示文摘Obtaining a highly synergistic mechanical property between joint and base metal(BM)in aluminum(Al)alloy is a chronic problem.In this work,shear bonding technology is applied to a commercial 6061 Al alloy.The results show that a flat and uniform joint interface is obtained.The joint presents a highly synergistic mechanical property compared with BM,whether after shear bonding or heat treatment.The joint coefficient reaches 95.6%after shear bonding and exceeds 100%after heat treatment,which is better than the traditional connection method of aluminum alloy.The high joint coefficient mainly originates from the well-linked joint and gradient grain structure.The gradient grain structure is beneficial to activate more slip systems to coordinate plastic deformation.Although the fine-grained structure is sacrificed after heat treatment,higher strength and joint coefficient are obtained due to the higher work hardening.This newly developed method has a large potential for application to the infinite rolling of Al alloy sheets and can also be used for Al alloy connection in automobile,aerospace,rail transportation,and other fields.The findings in this work can provide essential theoretical support and application reference for the shear connection of Al alloy. | Peng Peng Jian Su Qingsong He Ruinan Chen Sensen Chai Daliang Yu Qingwei Dai Jian Lu | 2023 | Journal of Materials Science & Technology2023，，33： | 0 |
| 4 | Microstructures,mechanical properties and degradability of Mg-2Gd-0.5(Cu/Ni)alloys:A comparison study显示文摘Low alloying Mg-2 Gd-0.5(Cu/Ni)alloys for sealing tools in the oil and gas industry were prepared.The differences in the effects of minor Cu and Ni additions on microstructures and properties of the Mg-2 Gd alloy were compared.The results showed that adding Ni was more effective than adding Cu in refining grain sizes,strengthening the basal fiber texture,and promoting the formation of LPSO phases,resulting in higher strength.The tensile yield strength/elongation of the Mg-2 Gd-0.5 Cu alloy,Mg-2 Gd-0.25 Cu-0.25 Ni alloy,and Mg-2 Gd-0.5 Ni alloy was 146 MPa/23.7%,175 MPa/23.1%,and 248 MPa/18.2%,respectively.The decreased elongation was attributed to the basal fiber texture and the presence of coarse LPSO phases.In terms of the corrosion rate in 3.5 wt.%NaCl solution,it rose from 112 mm y^(-1)for the Mg-2 Gd-0.5 Cu alloy to 269 mm y^(-1)for the Mg-2 Gd-0.25 Cu-0.25 Ni alloy and 490 mm y^(-1)for the Mg-2 Gd-0.5 Ni alloy,indicating that the addition of Ni instead of Cu showed a more significant promoting effect on the degradability of Mg alloys,which was related to more refined grains,the stronger basal fiber texture,and a larger amount of LPSO phases. | Shiyu Zhong Dingfei Zhang Yongqin Wang Sensen Chai Jingkai Feng Yulun Luo Jianrong Hua Qimin Dai Guangshan Hu Junyao Xu Bin Jiang Fusheng Pan | 2022 | Journal of Materials Science & Technology2022，，33： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员