题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Dynamic Recrystallization of a Cr-Ni-Mo-Cu-Ti-V Precipitation Hardenable Stainless Steel显示文摘在这研究,当演员组猛冲的动态再结晶(DRX ) 行为可硬化(PH ) 不锈钢被在在 950-1150 ° C 之间并且在 DRX 负责流动在热压缩期间弄软的 0.001-1 s_1.The 流动压力曲线表演的紧张率下面的温度进行热压缩测试调查。紧张和相应于流动曲线的山峰点(epsilon_p 和 sigma_p ) 的应力上的温度和紧张率的效果个别地被分析。这被认识到,他们与温度与紧张率和减少增加。在 Zener-Hollomon 参数(Z) 和 epsilon_p 之间的关系被调查并且 epsilon_p=4.3x10~ 的方程(-4)Z^(0.14 ) 被建议。为 DRX (epsilon_( 最大)) 的最大的率的紧张在不同变丑条件下面被决定。因此,它与 Z 参数和钳子增加,这被认识到。根据获得的结果, epsilon_( 最大) 的方程 =9.5x10^(-4)z^(0.12 ) 被建议。 | A.Momeni A.Shokuhfar S.M.Abbasi | 2007 | Journal of Materials Science & Technology2007，23，6： | 6 |
| 2 | 热加工和后处理对Ti-6Al-4V合金显微组织和拉伸性能的影响(英文)显示文摘研究了热压缩、热轧制和后续轧制退火处理对Ti-6Al-4V合金显微组织和拉伸性能的影响。热压缩实验在温度800~1075°C和应变速率0.001~1s-1下进行,得到了流变曲线与加工过程参数之间的关系。然后,样品在温度800~1070°C和恒应变速率2s-1下进行2道次热轧制,总变形量为75%。热轧后,样品分别在870°C和920°C下保温热处理2h,随后空冷。在β相区的热轧导致粗大的β相冷却时转变为马氏体相,而在α/β两相区的热轧会导致生成部分球化的α相组织。后续的热轧处理能使在两相区部分球化的α相得以完成球化,然而,在β相区轧制的样品会导致马氏体结构被破坏。拉伸实验表明,随着轧制温度从两相区升高到单相区,合金的强度及伸长率会显著降低。升高热处理温度会降低两相区轧制合金的强度性能,而在β相区轧制合金的强度会得到提高。 | S.M.ABBASI A.MOMENI | 2011 | Transactions of Nonferrous Metals Society of China2011，21，8： | 5 |
| 3 | IMI834钛合金在热拉伸变形过程的流变行为建模(英文)显示文摘建立合适的本构模型预测IMI834钛合金在α+β区的热拉伸流变行为。热拉伸实验在温度为800~1025°C、应变速率为0.001~0.1 s-1条件下进行。此本构模型通过Arrhenius型方程来表征应变为0.08~0.22时合金的热拉伸行为。结果表明,在不同应变条件下IMI834钛合金的热拉伸变形激活能范围为519~557 k J/mol。利用标准统计参数估算预测合金流变应力曲线的精度。所预测的合金的流变应力曲线与实验结果十分吻合。 | M.H.GHAVAM M.MORAKABATI S.M.ABBASI H.BADRI | 2015 | Transactions of Nonferrous Metals Society of China2015，25，3： | 4 |
| 4 | Repetitive Thermomechanical Processing towards Ultra Fine Grain Structure in 301,304 and 304L Stainless Steels显示文摘Thermomechanical processing as a combination of cold rolling and annealing was performed on austenitic stainless steels 301,304 and 304L.Two cold rolling steps each one up to a reduction of 75% were combined with an intermediate annealing at 800 C for 20 min.The final annealing was performed at the same temperature and time.Cold rolling contributed to martensite formation at the expense of metastable austenite in the studied materials.Austenite in 301 was found to be less stable than that in 304 and 304L.Hence,higher strength characteristics in the as-quenched 301 stainless steels were attributed to the higher volume fraction of martensite.Both α-martensite and ε-martensite were found to form as induced by deformation.However,the intensity of ε-martensite increased as the stability of austenite decreased.Annealing after cold rolling led to the reversion of austenite with an ultra fine grained structure in the order of 0.5-1μm from the strain induced martensite.The final grain size was found to be an inverse function of the amount of strain induced martensite.The thermomechanical processing considerably improved the strength characteristics while the simultaneous decrease of elongation was rather low. | A.Momeni S.M.Abbasi | 2011 | Journal of Materials Science & Technology2011，27，4： | 2 |
| 5 | 热拉伸和压缩条件下铸造和锻造Ni-42Cu合金的热加工性能(英文)显示文摘为了分析铸造和锻造条件下Ni-42Cu合金的流变行为和热加工性能,在温度为900~1150°C、应变速率为0.001~1 s^(-1)的条件下对合金进行热变形实验。拉伸实验结果表明,950°C时铸造和锻造两种合金均出现'热塑性低谷'。因为慢速动态再结晶,铸造合金的热塑性降低更为明显。合金(特别是铸造合金)的热塑性降低、晶界开裂归因于枝晶原子向晶界的偏析。随应变速率的增大,锻造合金的热塑性得到提高,这与高应变速率下动态再结晶分数的增加有关。此结果验证了动态再结晶机理随应变速率而变化。计算得到锻造合金的应变速率敏感性和不稳定参数结果表明,此合金在低温如950~1050°C和高应变速率(0.1和1 s^(-1))条件下易发生应变集中。根据拉伸和压缩实验结果,合金获得理想热加工性能的最佳温度为1050~1150°C。 | M.ARJM S.M.ABBASI A.KARIMI TAHERI A.MOMENI | 2016 | Transactions of Nonferrous Metals Society of China2016，26，6： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员