| 1 | 面心纯铝轧制织构的晶体塑性有限元模拟显示文摘基于率相关晶体塑性本构模型,分别将Taylor模型和有限单元模型两种多晶模型嵌入大型有限元程序ABAQUS,实现了晶体塑性学有限元模拟.直接将电子背散射衍射(EBSD)获取的晶粒初始取向输入晶体塑性有限元模型,预测了两种不同应变情况下面心1050纯铝轧制织构的演化.模拟结果与EBSD实验测得的织构演化结果有较好的一致性,随着变形程度的增加,预测织构与实测织构变得更加锋锐.经过比较,Taylor型模型预测出了{4411}〈11118〉的Dillamore取向,而有限单元模型预测出了铜型织构取向,比Taylor模型预测结果更接近实验验证结果.两种模型并不能预测出{011}〈211〉黄铜取向、{123}〈523〉S取向、{011}〈100〉Goss取向及其他理想取向. | 皮华春 韩静涛 章传国 A. K. Tieu 姜正义 | 2007 | 北京科技大学学报2007，29，9： | 3 |
| 2 | 薄带冷轧接触力学(英文)显示文摘极薄带冷轧给轧制生产带来了挑战,其中包括接触力学、带材的凸度和表面质量。在考虑工作辊边部接触的前提下,采用自行开发的改良影响函数法对薄带的对称和非对称冷轧过程进行了分析。文章的重点是通过薄带冷轧来阐述辊缝接触力学,分析辊缝处的摩擦对轧制力学和带材凸度的影响,同时还对轧辊边部接触对轧制力学和带材凸度影响进行了讨论,认为轧辊边部接触将对工作辊边部磨损产生影响,并对轧制力计算值与实测值进行了比较。 | 姜正义 韦东滨 李贺杰 谢海波 朱洪涛 A. K. Tieu 刘相华 张晓明 | 2008 | 塑性工程学报2008，15，3： | 2 |
| 3 | Simulation of polycrystalline aluminum tensile test with crystal plasticity finite element method显示文摘The crystal plasticity was implemented in the finite element method(FEM) software ABAQUS through the user subroutine UMAT. By means of discretizing the space at the grain level with the Voronoi diagram method, a polycrystal model was built and used in the FEM analysis. The initial orientation of each grain was generated based on the orientation distribution function(ODF). The developed model was successfully applied in simulation of polycrystalline aluminium samples deformed by the tensile tests. The theoretical strain—stress relation was in good agreement with the experimental result. The simulation results show that the grain size has significant effect on the deformation behavior. The initial plastic deformation usually occurs at grain boundaries, and multiple slip often results in an enhanced local hardening at grain boundaries. | 司良英 吕程 K. Tieu 刘相华 | 2007 | 中国有色金属学会会刊:英文版2007，17，6： | 2 |
| 4 | High-temperature creep-deformation behavior of the Ni-based superalloy M963显示文摘 | L. Z. He Q. Zheng X. F. Sun H. R. Guan Z. Q. Hu A. K. Tieu C. Lu H. T. Zhu | 2005 | Metallurgical and Materials Transactions A2005，，9： | 1 |
您所在的机构暂未开通此部分的功能，请联系管理员