| 1 | NUMERICAL SIMULATION OF INDUCTION SKULL MELTING PROCESS FOR TITANIUM-ALUMINIUM BASE ALLOY显示文摘The mathematics model for temperature field of water-cooling copper crucible induction skull melting process was established. The program for simulating temperature field of melting process was developed with finite element method. The temperature field of the melting process for Ti-47Al-2Cr-2Nb alloy was calculated. During melting period, the temperature is raised gradually along radius augmentation direction. The elements of the charge near the crucible wall are molten first. The center elements of the charge are molten last. The melting time of the center element is just that of all the charge melting. The melting time of Ti-47Al-2Cr-2Nb alloy is 15min. In which, the charge was heated by low power 80kW for 9min and by high power 300kW for 6min. When melting Ti-47Al-2Cr-2Nb alloy, the loading power is nearly direct proportion to melt temperature. Increasing loading power may raise melt temperature. The best melting power of Ti-47Al-2Cr-2Nb alloy is 305-310kW. This is identical with the melting test and has guidance sense to the melting process of actual titanium alloy. | Z.Y.Chen L.J.Xu F.T.Kong Q.Shu Y.Y.Chen | 2004 | Acta Metallurgica Sinica(English Letters)2004，17，6： | 2 |
| 2 | Effect of 2–6 at.% Mo addition on microstructural evolution of Ti-44Al alloy显示文摘In order to understand the effect of Mo alloying on the microstructural evolution of TiAl alloy, the as-cast microstructure, heat treated microstructure characteristic, and hot compression microstructure evolution of Ti-44 A1 alloy have been studied in this work. The as-cast microstructure morphology changes from(γ+α_2)lamellar colony and β/β_0+γ mixture structure to β/β_0 phase matrix widmannstatten structure,when Mo content increases from 2 at.% to 6 at.%. Affected by the relationship between β phase and αphase, the angles between the lamellar orientation and the block β/β_0 phase are roughly at 0°, 45° and90°. Comparing with heat treatment microstructure, the hot compression microstructure contains lessβ/β_0 phase, however, the β/β_0 phase containing 2 Mo alloy and 3 Mo alloy hot compressed at 1275 ℃ has the inverse tendency. In addition,(α_2 +γ) colony is decomposed by the discontinuous transformation. | S.Z.Zhang Z.W.Song J.C.Han C.J.Zhang P.Lin D.D.Zhu F.T.Kong Y.Y.Chen | 2018 | Journal of Materials Science & Technology2018，34，7： | 1 |
您所在的机构暂未开通此部分的功能，请联系管理员