|
|
|
题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Microstructural evolution and mechanical properties of Mg-9.8Gd-2.7Y-0.4Zr alloy produced by repetitive upsetting显示文摘A newly developed severe plastic deformation(SPD) technique, i.e. repetitive upsetting(RU), is employed to improve the strength and ductility of a Mg-Gd-Y-Zr alloy. During the RU processing, dynamic recrystallization occurs in the Mg alloy, which leads to a significant grain refinement from 11.2 μm to 2.8 μm.The yield strength(YS), ultimate tensile strength(UTS) and elongation increase simultaneously with increasing RU passes. The microstructural evolution is affected by processing temperatures. Dynamic recrystallization prevails at low temperatures, while dynamic recovery is the main effect factor at high temperatures. Texture characteristics gradually become random during multiple passes of RU processing,which reduces the tension-compression asymmetry of the Mg-Gd-Y-Zr alloy. | H.Zhou H.Y.Ning X.L.Ma D.D.Yin L.R.Xiao X.C.Sha Y.D.Yu Q.D.Wang Y.S.Li | 2018 | Journal of Materials Science & Technology2018，34，7： | 6 |
| 2 | Effect of Y content and equal channel angular pressing on the microstructure, texture and mechanical property of extruded Mg-Y alloys显示文摘The microstructure, texture and mechanical property evolution of the extruded Mg-x Y(x = 1, 5 wt.%) alloys during equal channel angular pressing(ECAP) were systematically investigated using an optical microscope, electron backscatter diffraction(EBSD) and uniaxial tensile test. The Mg-Y alloys exhibited a weakened basal texture before the ECAP, and the texture was further weakened with the max basal poles dispersed along ~45° between the extrusion direction and the transverse direction after the ECAP. The Mg-5 Y alloys always exhibited a finer grain size comparing to that of Mg-1 Y for the same ECAP process. With a proper ECAP process, both the strength and elongation of Mg-5 Y alloy could be improved simultaneously after the ECAP, i.e., the yield strength(273.9 ± 1.2 MPa), ultimate strength(306.4 ± 3.0 MPa),and elongation(23.9 ± 1.0%) were increased by 10%, 6%, and 72%, respectively, comparing to that before the ECAP. This was considered to be arose from the combined effects of grain refinement, significant improved microstructure homogeneity and solid solution hardening.In addition, it was found that Mg-Y alloy with better comprehensive properties could be obtained by the decreasing-temperature ECAP processes. The yield strength-grain size relationship could be well described by the Hall-Petch relation for all the ECAPed Mg-Y alloys,which was consistent with that the texture changes did not significantly affect the average Schmid factors of basal, prismatic and pyramidal slips for both Mg-Y alloys. | W.Yang G.F.Quan B.Ji Y.F.Wan H.Zhou J.Zheng D.D.Yin | 2022 | Journal of Magnesium and Alloys2022，10，1： | 6 |
| 3 | Effects of Y content and temperature on the damping capacity of extruded Mg-Y sheets显示文摘The damping behavior of extruded Mg-xY(x=0.5,1.0,3.0 wt.%)sheets were investigated in detail concerning the effects of Y addition and temperature,and the relationship between damping capacity and yield strength was discussed.At room temperature(RT),with Y content increasing from 0.5%to 3.0%,the damping capacity(Q-1)significantly decreased from 0.037 to 0.015.For all the studied sheets,the relationship between strain amplitude and Q-1 fitted well with the Granato and Liicke(G-L)dislocation damping model.With temperature increased,the G-L plots deviated from linearity indicating that the dislocation damping was not the only dominate mechanism,and the grain boundary sliding(GBS)could contribute to damping capacity.Consequently,the Q-1 increased remarkably above the critical temperature,and the critical temperature increased significantly from 50℃ to 290℃ with increasing Y contents from 0 to 3.0wt.%.This result implied that the segregation of Y solutes at grain boundary could depress the GBS,which was consistent with the recent finding of segregation tendency for rare-earth solutes.The extruded Mg-IY sheet exhibited slightly higher yield strength(Rp0.2)and Q-1 comparing with high-damping Mg-0.6Zr at RT.At an elevated temperature of 325℃,the Mg-IY sheet had similar Q-1 but over 3 times larger Rp0.2 than that of the pure Mg.The present study indicated that the extruded Mg-Y based alloys exhibited promising potential for developing high-performance damping alloys,especially for the elevated-temperature application. | Y.T.Tang C.Zhang L.B.Ren W.Yang D.D.Yin G.H.Huang H.Zhou Y.B.Zhang | 2019 | Journal of Magnesium and Alloys2019，7，3： | 5 |
您所在的机构暂未开通此部分的功能，请联系管理员