Insight into atmospheric corrosion evolution of mild steel in a simulated coastal atmosphere

查看全文 作　　者：Yue [1,2]Wang;Xin [1]Mu;Junhua [1]Dong;Aniefiok Joseph [1,2]Umoh;Wei [3]Ke 高影响力作者 机构地区：[1]Shenyang National Laboratory for Materials Science,Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China;[2]School of Materials Science and Engineering,University of Science and Technology of China,Shenyang 110016,China;[3]Environmental Corrosion Centre of Materials,Institute of Metal Research,Chinese Academy of Sciences,Shenyang 110016,China高影响力机构 出　　处：《Journal of Materials Science & Technology》索引2021年第17期,共10页高影响力期刊 基　　金：financially the Natural Science Foundation of Liaoning Province,China(No.2019JH3/30100037);the National Natural Science Foundation of China(No.51671200);the State Key Laboratory of Metal Material for Marine Equipment and Application(No.SKLMEA-K201907)。 摘　　要：The corrosion behavior of mild steel in a simulated coastal atmosphere environment has been investigated by the indoor accelerated wet/dry cyclic corrosion acceleration test(CCT),scanning electron microscopy(SEM),Raman spectroscopy and electrochemical measurements.During the CCT test of 60 cycles,the evolution of logarithmic(corrosion rate)vs.logarithmic(CCT cycles)presents a turning point at the 5th cycle,presenting a tendency to increase first and then decrease to gradually stabilize as the CCT cycle prolonged.Before the 5th cycle,γ-FeOOH andβ-FeOOH and Fe_(3)O_(4)were detected,respectively.And then,α-FeOOH as a new chemical composition was detected in the subsequent corrosion cycles.It is found that,after long term corrosion,the rust separated into a relatively dense inner layer rich withα-FeOOH and a loose outer layer rich withγ-FeOOH,both of which have poor electrical conductivity.The rapid increase of corrosion rate in the early stage since reducible corrosion products are involved in the reduction process of the cathode which promotes the dissolution of the anodic metal substrate.Afterward,as the rust layer thickens,the resistance of the rust increases,and the aggressive ions diffusion is blocked,gradually suppressing the electrochemical corrosion process.At last,when the composition and distribution of the rust layer remain stable,the corrosion presents a fluctuating speed around a certain value during the cracking and self-repairing process of the rust layer. 关 键 词：Mild steel Coastal atmospheric corrosion Raman spectroscopy Rusting evolution EIS
相关文献

参考文献(48)

引证文献(14)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费