In situ growth of single-crystal TiO2 nanorod arrays on Ti substrate: Controllable synthesis and photoelectro- chemical water splitting

查看全文 作　　者：Tingting [1,2]Zhang;Zia Ur [1]Rahman;Ning [3]Wei;Yupeng [1]Liu;Jun [1]Liang;Daoai [1,3]Wang

机构地区：[1]State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy ofSciences, Lanzhou 730000, China;[2]University of Chinese Academy of Sciences, Beijing 100049, China;[3]Qingdao Center for Resource Chemistry and New Materials, Qingdao 266100, China

出　　处：《Nano Research》索引2017年第10卷第3期,共12页

基　　金：Thanks for the financial support of the National Natural Science Foundation of China (Nos. 21303227, 21573259, and 51403220), Qingdao science and tech- nology plan application foundation research project(No. 14-2-4-60-JCH) and the "Hundred Talents Pro- gram" of Chinese Academy of Sciences (D. A. W.). 摘　　要：尽管有一个维(1D ) 半导体 nanostructure 数组吸引由于他们的许多增加注意有利,高度订的 TiO ₂ nanorod 数组(TiO ₂ NR ) 很少在 Ti 底层上在 situ 被种。此处,由使用一个通过面具阳极化过程在 Ti 底层上制作 TiO ₂ NR 的一个可行方法被报导。在 Ti 底层上覆盖的自我命令的阳极的铝氧化物(AAO ) 被用作 nanotemplate 导致 TiO ₂ NR 的生长。NR 长度和直径能被调整象电气化学的阳极化电压,阳极化时间和温度那样的阳极化参数控制,并且电解质作文。根据建议 NR 形成机制,而且,阳极化的 Ti 离子移居并且在 AAO nanochannels 扔形成 Ti (哦) 在电场下面的 ₄ 或非结晶的 TiO ₂ NR,由于模板的监禁效果。Photoelectrochemical 测试显示在加氢以后, TiO ₂ NR 在模仿的日光和可见轻照明下面介绍了更高的光电流密度,建议他们在 photoelectrochemical 水切开,光催化,太阳能电池,和传感器的潜在的使用。 关键词：加氢 TiO ₂ nanorod 数组在 situ 准备通过洞 AAO 面具 PHOTOELECTROCHEMICAL

相关文献

参考文献（39）
引证文献（4）
耦合文献（15）

参考文献(39)

引证文献(4)

耦合文献(15)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

In situ growth of single-crystal TiO2 nanorod arrays on Ti substrate: Controllable synthesis and photoelectro- chemical water splitting

参考文献(39)

引证文献(4)

耦合文献(15)

用户提示