Processing map for hot working of SiC_p/7075 Al composites

查看全文 作　　者：[1]M.RAJAMUTHAMILSELVAN;[1]S.RAMANATHAN;[2]R.KARTHIKEYAN

机构地区：[1]Department of Manufacturing Engineering,Annamalai University;[2]Department of Mechanical Engineering,Birla Institute of Technology and Sciences

出　　处：《Transactions of Nonferrous Metals Society of China》索引2010年第20卷第4期,共7页

摘　　要：The hot deformation behaviour of 7075 aluminium alloy reinforced with 10%of SiC particles was studied by employing both'processing maps'and microstructural observations.The composite was characterized by employing optical microscope to evaluate the microstructural transformations and instability phenomena.The material investigated was deformed by compression in the temperature and strain rate ranges of 300-500℃and 0.001-1.0 s-1,respectively.The deformation efficiency was calculated by strain rate sensitivity(m)values obtained by hot compression tests.The power dissipation efficiency and instability parameters were evaluated and processing maps were constructed for strain of 0.5.The optimum domains and instability zone were obtained for the composites.The optimum processing conditions are obtained in the strain rate range of 0.1-0.9 s-1and temperature range of 390-440 ℃with the efficiency of 30%. 关键词：hot deformation processing maps RECRYSTALLIZATION flow instability

相关文献

参考文献（24）
引证文献（9）
耦合文献（0）

参考文献(24)

引证文献(9)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Processing map for hot working of SiC_p/7075 Al composites

参考文献(24)

引证文献(9)

用户提示